No matter what industry you work in, we are exposed to millions of bacteria each day which can cause infections.

We take pride in manufacturing and providing the following types of gloves to our clients:

Non-Sterile Latex Examination Powder Free Gloves

Evergreen Latex Natural Latex Gloves

Tensile Properties

Properties Requirements
Minimum force at break before accelerated ageing, N 7,0
Minimum force at break after accelerated ageing, N 6,0
Minimum elongation at break before accelerated ageing, % 650
Minimum elongation at break after accelerated ageing, % 500
Evergreen Natrual Latex Examination Glove

Textured Surface(mm)
Thickness: Middle finger: 0.11 Min | Centre of palm: 2.03 Max | Cuff: 2.50 Max
Weight: ±5.5g and ±6.5g

Non-Sterile High Risk Powder Free Gloves

Evergreen Latex High Risk Examination Gloves Packaging

Tensile Properties

Properties Requirements
Minimum force at break before accelerated ageing, N 7,0
Minimum force at break after accelerated ageing, N 6,0
Minimum elongation at break before accelerated ageing, % 650
Minimum elongation at break after accelerated ageing, % 500
Evergreen Latex High Risk Examination Gloves

Textured Surface(mm)
Thickness: Middle finger: 0.11 Min | Centre of palm: 2.03 Max | Cuff: 2.50 Max
Weight:±13.0g

Non-Sterile Nitrile Powder Free Examination Gloves

Evergreen Latex Nitrile Disposable Gloves

Tensile Properties

Properties Requirements
Minimum force at break before accelerated ageing, N 7,0
Minimum force at break after accelerated ageing, N 7,0
Minimum elongation at break before accelerated ageing, % 500
Minimum elongation at break after accelerated ageing, % 400
Evergreen Latex Nitrile Disposable Glove

Textured Surface(mm)
Thickness: Middle finger: 0.11 Min | Centre of palm: 2.03 Max | Cuff: 2.50 Max
Weight: ±3.5g

Sterile Latex Elbow Length Powder Free Examination Gloves

Evergreen Latex Elbow Length Powder Free Gloves

Tensile Properties

Properties Requirements
Minimum force at break before accelerated ageing, N 7,0
Minimum force at break after accelerated ageing, N 6,0
Minimum elongation at break before accelerated ageing, % 650
Minimum elongation at break after accelerated ageing, % 500
Evergreen Elbow Length Examination Gloves

Textured Surface(mm)
Thickness: Middle finger: 0.11 Min | Centre of palm: 2.03 Max | Cuff: 2.50 Max
Weight: ±22g

Surgical Latex Powder Free Gloves

Evergreen Latex Surgical Gloves

Tensile Properties

Properties Requirements
Minimum force at break before accelerated ageing, N 12,5
Minimum force at break after accelerated ageing, N 9,5
Minimum elongation at break before accelerated ageing, % 700
Minimum elongation at break after accelerated ageing, % 550
Maximum force required to produce 300% elongation before accelerated ageing, N 2,0
Evergreen Latex Surgical Gloves Cure X

Textured Surface(mm)
Thickness: Middle finger: 0.13 Min | Centre of palm: 0.13 Min | Cuff: 2.50 Max
Weight: ±10g

Sterile Nitrile Powder Free Examination Gloves

Evergreen Latex Sterile nitrile examination gloves

Tensile Properties

Properties Requirements
Minimum force at break before accelerated ageing, N 7,0
Minimum force at break after accelerated ageing, N 7,0
Minimum elongation at break before accelerated ageing, % 500
Minimum elongation at break after accelerated ageing, % 400
Evergreen Nitrile Powder Free Examination Gloves

Textured Surface(mm)
Thickness: Middle finger: 0.11 Min | Centre of palm: 2.03 Max | Cuff: 2.50 Max
Weight: ±3.5g

Sterile Latex Powder Free Examination Gloves

Evergreen Sterile Powder Free Examination Gloves

Tensile Properties

Properties Requirements
Minimum force at break before accelerated ageing, N 7,0
Minimum force at break after accelerated ageing, N 6,0
Minimum elongation at break before accelerated ageing, % 650
Minimum elongation at break after accelerated ageing, % 500
Evergreen Sterile Powder Free Examination Gloves

Textured Surface(mm)
Thickness: Middle finger: 0.11 Min | Centre of palm: 2.03 Max | Cuff: 2.50 Max
Weight: ±5.5g

Isoprene surgical gloves: Glov’em in isoprene 

0Tensile Properties

Properties Requirements
Minimum force at break before accelerated ageing, N 9,0
Minimum force at break after accelerated ageing, N 9,0
Minimum elongation at break before accelerated ageing, % 600
Minimum elongation at break after accelerated ageing, % 500
The maximum force required to produce 300%melengation before accelerated ageing. 3.0
Evergreen Sterile Powder Free Examination Gloves

Textured Surface(mm)
Thickness: Middle finger: 0.22 ± 0.02 | Centre of palm: 0.19 ± 0.02 | Cuff: 0.17 ±0.02
Weight: ±16g

Chloreprene surgical gloves: Glov’em in isoprene

60Tensile Properties

Properties Requirements
Minimum force at break before accelerated ageing, N 9,0
Minimum force at break after accelerated ageing, N 9,0
Minimum elongation at break before accelerated ageing, % 600
Minimum elongation at break after accelerated ageing, % 500
The maximum force required to produce 300%melengation before accelerated ageing. 3.0
Evergreen Sterile Powder Free Examination Gloves

Textured Surface(mm)
Thickness: Middle finger: 0.20 Min | Centre of palm: 0.17 ± 0.02 | Cuff: 015 ± 0.02 
Weight: ±15g